Sr2CaCu2O8+x superconducting ceramics have been irradiated in the scanning electron microscope (SEM), and the irradiation-induced effects investigated by cathodoluminescence (CL), secondary electron emission (SEE) and X-ray microanalysis. Electron beam irradiation causes a slight Bi depletion and an inhomogeneous Ca distribution. A higher CL intensity emission is found in the irradiated areas, where besides an enhancement of the oxygen content related 2. 4 eV band, another CL bands probably related to new non-superconducting phases induced by irradiation can be observed. SEE yield measurements allow to detect an oxygen depleted region surrounding the irradiated areas. X-ray microanalysis shows that this intermediate region retains the cationic composition of the unaffected material. CL spectra from bright zones inside the same area also show a dominant 2. 4 eV emission band, which supports its relation with oxygen deficiency or rearrangement in high-\(\) superconductors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Applied Physics A: Materials Science & Processing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.