Abstract
Fatigue crack growth (FCG) mechanisms have been studied in light of the interaction of a propagating crack with local crystallographic orientations of primary alpha (αP) and secondary alpha (αS) colonies in a near α Timetal 834 Ti-alloy under thermomechanical fatigue (TMF) loading using electron backscattered diffraction (EBSD). FCG testing at in-phase (IP) and out-of-phase (OP) TMF loading have been carried out at two temperature intervals 300°C↔450°C and 450°C↔600°C. EBSD analysis and microhardness measurements have confirmed that larger cyclic plastic zone size at the crack tip leads to lower crack propagation under IP-TMFCG loading as compared to OP-TMFCG loading. EBSD analysis has also confirmed that crack dissipates more energy to propagate when it passes from a soft grain oriented with its c-axis normal to the loading direction and encounters a hard grain with its c-axis parallel with the loading direction.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.