Abstract
ABSTRACTThe electromigration lifetimes of a very large quantity of passivated electroplated Au interconnects were measured utilizing high-resolution in-situ resistance monitoring equipment. Application of moderate accelerated stress conditions with current density limited to 2 MA/cm2 and oven temperatures in the range of 300°C to 375°C prevented large Joule-heated temperature gradients and electrical overstress failures. A Joule-heated Au film temperature increase of 10°C on average was determined from measured temperature coefficients of resistance (TCRs). A failure criterion of 50% resistance degradation was selected to avoid thermal runaway and catastrophic open circuit failures. All Au lifetime distributions followed log-normal statistics. An activation energy of 0.80 ± 0.05 eV was measured from constant-current electromigration tests at multiple temperatures. A current density exponent of 1.91 ± 0.03 was extracted from multiple current densities at a single constant temperature.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call