Abstract
The composite approach, by incorporating small amounts of reinforcement particles in the solder matrix, has proven to be one of the effective ways to improve the reliability of solder joints. The effects of Cu addition on electromigration were investigated in this study by incorporating 2% volume fraction Cu particles into Sn-3.5Ag eutectic solder paste by the in situ process. The one-dimensional solder joints, designed to prevent the current crowding effect, were stressed under a constant current density of 104 A/cm2 at room temperature, and the temperature of the sample could reach 105 ± 5°C due to the Joule heating effect. Doping 2 vol.% Cu was found to retard the electromigration phenomenon effectively. After electric current stressing for 528 h, the growth rate of an interfacial intermetallic compound (IMC) layer at the anode decreased 73% in contrast to that of Sn-3.5Ag solder joints, and the IMC layer at the cathode was almost unchanged. The polarization effect of Cu reinforced composite solder joints was also apparently mitigated. In addition, the surface damage of the composite solder joints was relieved by incorporating 2 vol.% Cu particles. Compared to Sn-3.5Ag solder joints, which had protruded Cu6Sn5 and wrinkles of Sn-solder matrix on the surface, the solder joints with Cu addition had a more even surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.