AbstractAtom movements of Cu in pure Cu and Cu(0.5 to 2 wt.% Sn) alloys have been investigated using drift velocity and radioactive tracer techniques. The void growth rate in pure Cu at the cathode end, as a result of electromigration driving force, linearly increases with the applied current density. A marked decrease in the Cu grain boundary diffusivity and electromigration drift velocity is attributed to Sn trapping of Cu atoms and/or binding defects at grain boundaries. The effect is more pronounced at lower temperatures. The activation energies for electromigration and diffusion of Cu in pure Cu grain boundaries were found to be in the range of 0.7 - 0.9 eV. Addition of about 0.5 to 2 wt.% Sn increased these energies to 1.1 - 1.3 eV, respectively which resulted in enhancement of electromigration resistance by several orders of magnitude over that in pure Cu at the field operation temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.