Abstract
Piezoelectric composites are a significant research field because of their excellent mechanical flexibility and sufficient stress-induced voltage. Furthermore, due to the widespread use of the Internet of Things (IoT) in recent years, small-sized piezoelectric composites have attracted a lot of attention. Also, there is an urgent need to develop evaluation methods for these composites. This paper evaluates the piezoelectric and mechanical properties of potassium sodium niobate (KNN)-epoxy and KNN-glass fiber-reinforced polymer (GFRP) composites using a modified small punch (MSP) and nanoindentation tests in addition to d33 measurements. An analytical solution for the piezoelectric composite thin plate under bending was obtained for the determination of the bending properties. Due to the glass fiber inclusion, the bending strength increased by about four times, and Young's modulus in the length direction increased by approximately two times (more than that of the KNN-epoxy); however, in the thickness direction, Young's modulus decreased by less than half. An impact energy harvesting test was then performed on the KNN-epoxy and KNN-GFRP composites. As a result, the output voltage of KNN-GFRP was larger than that of KNN-epoxy. Also, the output voltage was about 2.4 V with a compressive stress of 0.2 MPa, although the presence of the glass fibers decreased the piezoelectric constants. Finally, damped flexural vibration energy harvesting test was carried out on the KNN-epoxy and KNN-GFRP composites. The KNN-epoxy was broken during the test, however KNN-GFRP composite with a load resistance of 10 MΩ generated 35 nJ of energy. Overall, through this work, we succeeded in developing piezoelectric energy harvesting composite materials that can withstand impact and bending vibration using glass fibers and also established a method for evaluating the electromechanical properties with small test specimen.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.