Abstract
Abstract The solid waste material cenosphere (fly ash, by-product of thermal power plants) was nickel oxide nanoparticle coated (NiOC, core shell structure) by chemical heterogeneous precipitation and thermal reduction method. in situ synthesis of polyaniline (PANI) and NiOC composite (PNiOC) was carried out at -30±2 °C under nitrogen and characterized. The free standing films of as synthesized PNiOC composite were prepared by solution casting (followed by acid vapor treatment) and electromagnetic interference (EMI) shielding effectiveness (SE) was investigated in the J-band (5.8–8.2 GHz), X-band (8.2–12.4 GHz) and Ku-band (12.4–18 GHz). An average EMI SE of ~24 dB, ~27–24 dB, ~21 dB was observed for 81±3 μm thicker flexible free standing PNiOC film in the J, X and Ku-band respectively. Effective EMI shielding due to absorption (SE A ) was found to be dominant for PNiOC film. Unlike PANI emeraldine salt (ES) film, the EMI shielding due to absorption (SE A ) was found more than two times higher for PNiOC film. Due to the presence of NiOC hollow microspheres in PANI, the time average power of incident electromagnetic wave decreases resulting in an increase of EMI SE (SE A ). This film can be considered as a novel coating material for various applications such as unmanned vehicles, robotic and microwave engineering to protect against EMI.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.