Abstract
The purpose of this article is to introduce the Co–Zn–P film coated on the nanodiamond cores by electroless deposition. The surface morphology, composition and magnetic performance of the coatings are studied with the help of transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), an energy dispersive X-ray detector (EDX) and the vibrating sample magnetometer (VSM). The results showed that the change of film composition and magnetic characteristics were dependant on the content of Cobalt, Zinc and Phosphorus. Evidently the coercive force was affected by the atomic composition of alloy film While the best proportion (the optimal composition mass ratio of Cobalt and Zinc was 1:4) in alloy film, the alloy film has good electromagnetic properties, even though the Phosphorus wt.%≥3%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.