Cu-coated Ti3SiC2 powder was fabricated by electroless copper plating method from CuSO4 using poisonless ascorbic acid (C6H6O4(OH)2) as reducing agent. Sensibilization and activation on Ti3SiC2 powder surface was performed by Sn-Ag catalyst system. Surfactants lauryl sodium sulfate (SDS) and Polysorbate 80 (Tween-80) were used as modifiers to control copper particle sizes and shapes. It is found that good pretreatment and activation can obtain fully-formed copper coating. The optimal copper deposition rate can reach to 2.053 g.dm-2.h-1 at 80°C . The best coating effect can be obtained in the samples modifying with 12g/L SDS+8ml/L Tween-80.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.