Abstract
Cu-Se binary compound films have been prepared by electrodeposition from solutions containing CuSO4, H2SeO3, and H2SO4 and their composition, structure, and thermoelectric performance analyzed. Moving the depositing potential negatively increased the Cu content in the film, remarkably so for relatively low Cu2+ concentration in the solution. X-ray diffraction analysis showed that the phase composition of the films varied with their Cu content. Cu-Se binary compound films electrodeposited from solutions with different concentration ratios of CuSO4 to H2SeO3 showed two different phases: α-Cu2−x Se (monoclinic) with Se content in the range of 33.3 at.% to 33.8 at.%, and β-Cu2Se (cubic) with Se content in the range of 35.3 at.% to 36.0 at.%. The highest power factor for electrodeposited Cu2−x Se film was 0.13 mW/(K2 m) with Seebeck coefficient of 56.0 μV/K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.