Abstract
Aluminum mandrel was electrolyzed in 1 mol/L sodium hydroxide solution using the electrolytic corrosion device. The relationship between voltage and current was got by changing the voltage (4-28 V). The surface of aluminum was absolutely passivated when the voltage was higher than 28 V. Activation energy was obtained from data fitted by changing the electrolyte temperature (20-35 ℃). Images of surface passivation samples and non-passivated sample were got from SEM. Non-passivated and passivated samples were analyzed and characterized by XRD. The main component of surface passivation layer was bayerite. Surface reaction process and passivated mechanism were inferred from the main component of passivation product.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.