Abstract

We have developed an artificially controllable strategy of an electrodeposition process adequate for resistive random-access memory (ReRAM) applications of binary Cu2O. Typically, the precise control of OH- ion concentration (the intermediate supplier of oxygen ions) at the electrode's surface decides the overall reaction rate of the Cu2O. Here, the suggested Pb and Sb metal additives preferentially contribute to the consumption of OH- ions and the supply of OH- ions, respectively, during the Cu2O electrochemical reaction so that the final products are the (200) preferential quadrangular pyramids and the (111) preferential triangular pyramids. Interestingly, the coexistence of Sb/Pb precursors in the Cu electrolytes results in extraordinarily decreased reaction rate from the opposite action of OH- ion utilization as well as intense progressive growth behavior, and the resultant Cu2O films consist of crystallized small-size nanoparticles (NPs) in an amorphous-like matrix. In the case of ReRAM applications, while the polycrystalline film induces irregular device performance and the amorphous layer shows an easily irreparable electrical breakdown, our NP-assembled Cu2O films from Pb/Sb metal ions reveal the formation of a conduction bridge via phase change to a crystalline filament with no need for forming voltage and with superior electrical stability. It is attributed to the coalescence of crystal NPs into large grains during the set/reset cycle process for the heat dissipation of Joule heating. The Cu2O sample prepared with a 3 mM Sb + 3 mM Pb mixture solution exhibits forming-free ReRAM devices with high on/off resistance ratios of 1.2 × 104 and long-term electrical/thermal stability.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.