Abstract
The corrosion of Q235 carbon steel in the saturated calcium hydroxide solution containing chloride ions and sulfate ions are studied using electrochemical methods and wire beam electrode (WBE) sensor. The cyclic potentiodynamic polarization measurements showed that localized corrosion was mainly induced by the adsorption of chloride ions on the passive film. When the passive film is intact, sulfate ions are not corrosive to the passive film and it can inhibit the pitting initiation caused by the chloride ions. However, the WBE test results indicate that once a stable pit has already formed, sulfate ions cannot mitigate the pitting corrosion, and it can further promote the propagation of the major anodic area. Through the electrochemical impedance spectroscopy measurements, it can be found that the addition of sulfate ions in the solution containing chloride ions will not result in the rise of the general corrosion rate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.