Abstract
The electrochemical response of several alloys (stainless steel 316, Hastelloy C276, Inconel 600, and tantalum) was investigated in molten LiCl–Li2O (1 wt%) at 923 K while bubbling oxygen gas into the molten salt. Tafel and zero resistance ammeter (ZRA) electrochemical methods were used to measure electrochemical effects of oxidation processes at the surface of each alloy. The Tafel method required approximately 15 min and was, thus, applied only in intervals between periods of oxygen bubbling in the salt. ZRA measurements were made in real time, while the O2 was actively being bubbled into the salt. This method recorded both open circuit potential of the alloy relative to a Ni/NiO reference electrode and current between the alloy and the galvanically coupled platinum plate that served as the counter electrode. Both open circuit potential and galvanic oxidation current started to increase at the initiation of oxygen flow. Based on the observed oxidation current trend, it was inferred that the metals in order of increasing resistance to oxidation in molten LiCl–Li2O are as follows: tantalum < SS-316 < Inconel 600 < Haynes C276. Scanning electron microscopy images indicated formation of an oxide layer of thickness 560–3370 nm that correlates with the galvanic oxidation current measurements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.