Abstract
The reaction mechanism of Si electrodeposition in the ionic liquid trimethyl-n-hexylammonium bis(trifluoromethylsulfonyl) imide (TMHATFSI) with SiCl4 was investigated using an electrochemical quartz crystal microbalance (EQCM) and X-ray photoelectron spectroscopy (XPS). The deposited films were further characterized by Raman spectroscopy. The EQCM method measured the frequency change in situ during electrodeposition, whereas XPS provided the Si mass concentration in the electrodeposited films. By combining these results, the mass change due to SiCl4 reduction was estimated. Then, the current efficiency for Si electrodeposition at various potentials was evaluated. The calculated current efficiency was almost 100% when it was assumed that SiCl4 reduction progressed by four-electron electroreduction. The XPS and Raman results showed that the deposited films were composed primarily of amorphous Si with Si–Si bonds. Crystalline Si thin films were obtained after annealing in an Ar gas stream.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.