Abstract
IntroductionNickel-titanium rotary endodontic files have been commercially available for decades, but more recent innovations have introduced heat-treated and surface-treated files. This study investigated the corrosion properties of various nickel-titanium files in normal saline and sodium hypochlorite (NaOCl). MethodsTen different file brands of size 40 with a 0.04 taper were subjected to electrochemical testing in 0.9% NaCl (saline) and 5.25% NaOCl at room temperature. The Open Circuit Potential (OCP) was observed for 1 hour followed by a cyclic polarization test from −300 to 700 mV and back to −300 mV (vs OCP). Nonparametric ANOVA and a pairwise comparison (P < .05) were used for statistical analysis of the OCP at 1 hour and the corrosion current (Icorr) obtained via the cyclic polarization test. ResultsSignificant differences (P < .05) were found between files with respect to OCP and Icorr in both solutions. Nine files exhibited significantly greater (P < .05) Icorrs in NaOCl than in saline. Conversely, pitting corrosion was observed in the saline solution but not NaOCl. Weak and/or moderate correlations existed between OCP and Icorr measures in the 2 solutions. ConclusionSignificant differences in electrochemical properties were observed among the 10 brands of files. Overall, there was not a clear trend between conventional, heat-treated, or surface-treated files among OCP or Icorr in either solution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.