Carbon aerogel (CA) was prepared by a sol-gel polymerization of resorcinol and formaldehyde, and it was activated with KOH to obtain activated carbon aerogel (ACA). Specific capacitance of carbon aerogel and activated carbon aerogel was measured by cyclic voltammetry and galvanostatic charge/discharge methods in 6 M KOH electrolyte. Activated carbon aerogel showed higher specific capacitance than carbon aerogel (136 F/g vs. 90 F/g). In order to combine excellent electrochemical performance of activated carbon aerogel with pseudocapacitive property of manganese oxide, 7 wt% manganese oxide was doped on activated carbon aerogel by an incipient wetness impregnation method. For comparison, 7 wt% manganese oxide was also doped on carbon aerogel by an incipient wetness impregnation method. It was revealed that 7 wt% Mn-doped activated carbon aerogel (Mn/ACA) showed higher specific capacitance than 7 wt% Mn-doped carbon aerogel (Mn/CA) (168 F/g vs. 98 F/g). The enhanced capacitance of 7 wt% Mn-doped activated carbon aerogel was attributed to the outstanding electric properties of activated carbon aerogel as well as the faradaic redox reactions of manganese oxide.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.