Electrochemical performance of microporous and mesoporous activated carbons in neat and diluted 1-ethyl-3-methylimidazolium tetrafluoroborate

Abstract

Abstract 1-Ethyl-3-methylimidazolium tetrafluoroborate (EMIm·BF4), neat and diluted with propylene carbonate to 1 mol L−1, have been employed as electrolytes of electrical double-layer capacitors (EDLCs). The effects of microporosity and mesoporosity in activated carbon (AC) electrodes on the capacitive and resistive performances upon the use of neat and diluted EMIm·BF4 have been explored. In addition to cyclic voltammetry and galvanostatic charge–discharge tests, electrochemical impedance spectroscopy has been performed employing Kang's equivalent circuit model consisting of three resistances, three constant phase elements, and one bounded Warburg impedance. The overall impedance of the EDLC cell was separated into components of intrinsic resistance, bulk electrolyte, diffusion layer, and Helmholtz layer. The specific capacitance and the equivalent series resistance (ESR) of mesoporous AC were found to be highly dependent on the rate of ionic transfer. Lower cell voltage was identified as being responsible for lower specific capacitance and larger ESR of mesoporous AC, which was similarly seen in the neat and diluted EMIm·BF4, and could be alleviated by increasing the cell voltage. The inferior rate performance and the cell-voltage-dependent performance of mesoporous AC, which were more distinctly observed in the neat EMIm·BF4, could be attributed to the lower mobility of EMIm+ and BF4− in mesopores.