Abstract
Platinum thin films comprising nominally 1 to 20 atomic overlayers were formed on a gold-coated substrate using the self-terminating electrodeposition (STED) method. The platinum overlayer loading and morphology were characterized using X-ray Photoelectron Spectroscopy (XPS), Inductively Coupled Plasma – Optical Emission Spectroscopy (ICP-OES), Field Emission Scanning Electron Microscopy (FESEM), Cyclic Voltammetry (CV) and Chronoamperometry (CA). The durability of these platinum overlayer samples was estimated by subjecting the samples to ex-situ electrochemical potential cycling. The extent of platinum overlayer growth is lower than expected till four STED cycles and then increases non-linearly, leading to increased roughness. The shifts of platinum redox peaks in CVs and Pt4f signals in XPS spectra indicate surface-alloying of gold and platinum. After the durability test, the morphological evolution of platinum overlayers conforms with the extent of platinum dissolution estimated from CVs. Our results reveal that more than four STED cycles are needed to form platinum overlayers that meet the US Department of Energy (DOE) criteria for durability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.