Abstract
AbstractElectrochemical corrosion behavior of electroless Ni–P coating in NaCl and H2SO4 solutions were studied by potentiodynamic polarization curves and electrochemical impedance spectra techniques, as well as the corrosion morphology was characterized. The results indicate that electroless Ni–P coating with about 25 µm is stable in 30 days immersion in NaCl solution. Although it was corroded with prolonged immersion days, the corrosive medium has not penetrated through the coating. During the H2SO4 concentration ranging from 5 to 10%, the corrosion current density of electroless Ni–P coating increased due to the intensified anodic dissolution process; in 15% H2SO4 solution, electroless Ni–P coating shows obvious anodic passivation effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.