Interface reactions and film features of AZ91D magnesium alloy in pickling, activation and zinc immersion solutions have been investigated. The surface morphologies of the specimens were observed with scanning electron microscope (SEM). Electrochemical behaviors of AZ91D magnesium alloy in the baths of pickling, activation and zinc immersion were analyzed based on the open circuit potential (OCP) - time curves in various solutions. The results show that the corrosive rate in HNO 3 + CrO 3 or HNO 3 + H 3PO 4 pickling solution was more rapid than in KMnO 4 pickling–activation solution. Both α phase and β phase of the substrates were uniformly corroded in HNO 3 + CrO 3 or HNO 3 + H 3PO 4 pickling solution, the coarse surface can augment the mechanical occlusive force between the subsequent coatings and the substrates, so coatings with good adhesion can be obtained. In HF activation solution, the chromic compound formed via HNO 3 + CrO 3 pickling was removed and a compact MgF 2 film was formed on the substrate surface. In K 4P 2O 7 activation solution, the corrosion products formed via HNO 3 + H 3PO 4 pickling were removed, a new thin film of oxides and hydroxides was formed on the substrate surface. In KMnO 4 pickling–activation solution, a film of manganic oxides and phosphates was adhered on the substrate surface. Zinc film was symmetrically produced via K 4P 2O 7 activation or KMnO 4 pickling–activation, so it was good interlayer for Ni or Cu electroplating. Asymmetrical zinc film was produced because the MgF 2 film obtained in the HF activation solution had strong adhesive attraction and it was not suitable for interlayer for electroplating. However, the substrate containing compact MgF 2 film without zinc immersion was fit for direct electroless Ni–P plating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.