Electrochemical Behavior and Stress Corrosion Sensitivity of X70 Steel Under Disbonded Coatings in Korla Soil Solution

Abstract

The corrosion of X70 pipeline steel under a model disbonded coating was studied in a simulated solution of Korla soil by combining in situ electrochemical measurements at different locations in the crevice and stress corrosion cracking (SCC) sensitivity analyses in the corresponding simulated environments. The results from electrochemical impedance spectroscopy showed that the corrosion product resistance R t and charge transfer resistance R ct of X70 steel first increased and then decreased with increasing distance from the opening of the crevice in the disbonded coating. Scanning electron micrographs showed that pitting in the crevice became more severe at deeper locations in the crevice. Slow strain rate tests showed that the lowest SCC sensitivity of X70 steel was found at 15 cm away from the opening, and the highest SCC sensitivity was at the end of the crevice.