Abstract
Nickel oxide and yttria stabilised zirconia (NiO/YSZ) cermets have been prepared using a chemical co-precipitation of hydroxides. The influence of different factors on the microstructure, mechanical and electrochemical properties of the anode were investigated. The electrochemical tests were carried out on dense 8YSZ and 10Sc1CeSZ tapes (50x50x0.150 mm, Kerafol GmbH) with symmetrically screen-printed cathodes and anodes with a lateral dimension of 40x40 mm. The cells were sintered in co-firing. The anodes were characterized by impedance spectroscopy at open circuit potential and under current load at temperatures of 850-950{degree sign}C in hydrogen/steam atmosphere (H2:H2O=1:1). The electrode polarization resistance (Rp) of the spectra was identified and the influences of operating temperature (850{degree sign}C, 900{degree sign}C and 950{degree sign}C), current load and pH2O on impedance spectra of anode were discussed. The long-term stability of the cell with an anode prepared by co-precipitation was carried out over 1000 hours under current density of 430-450 mA/cm2@0.7V at temperature 850{degree sign}C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.