Electro-mechanical and Polarization-Induced Antibacterial Response of 45S5 Bioglass-Sodium Potassium Niobate Piezoelectric Ceramic Composites.

Abstract

Besides the excellent osteoconductivity and biocompatibility of 45S5 bioglass (BG), poor mechanical and electrical properties as well as susceptibility toward bacterial adhesion limit its widespread clinical applications. In this context, the present study investigates the effect of addition of piezoelectric sodium potassium niobate (Na0.5K0.5NbO3; NKN) on mechanical, dielectric, and antibacterial response of BG. BG-xNKN (x = 0, 10, 20, and 30 vol%) composites were synthesized at 800 °C for 30 min. The phase analyses using spectral techniques revealed the formation of the composite without any reaction between BG and piezoelectric ceramic NKN. The dielectric and electrical measurements were performed over a wide range of temperature (30-500 °C) and frequency (1 Hz-1 MHz) which suggests that space charge and dipolar polarizations are the dominant polarization mechanisms. The complex impedance analyses suggest that the average activation energies for grain and grain boundary resistances for BG-xNKN (x = 10, 20, and 30 vol%) composites are 0.59, 0.87, 0.94 and 0.76, 0.93, 1.06 eV, respectively. The issue of bacterial infection has been addressed by electrical polarization of the developed composite samples, at 20 kV for 30 min. Statistical analyses reveal that the viability of Gram-positive (S. aureus) and Gram-negative (E. coli) bacterial cells has been reduced significantly on positively and negatively charged BG-NKN composite samples, respectively. The qualitative analyses using the Kirby-Bauer test supports the above findings. Nitro blue tetrazolium and lipid peroxide assays were performed to understand the mechanism of such antibacterial response, which suggested that the combined effect of NKN addition and polarization significantly enhances the superoxide production, which kills the bacterial cells. Overall, incorporation of NKN in BG enhances the mechanical, electrical, and dielectric properties as well as improves the antibacterial response of polarized BG-xNKN composites.