Abstract

We have fabricated (Pr1−yYy)1-xCaxCoO3 (PYCCO) epitaxial films with various thicknesses by pulsed laser deposition on the SrLaAlO4 (SLAO) substrate that applied an in-plane compressive stress to the film, and investigated the temperature dependence of the electrical resistivity, ρ(T), of the films. An anomalous ρ(T) upturn with a broad hysteresis could be clearly observed only for the thinnest film (d = 50 nm), and the ρ(T) anomaly decreased by increasing film thickness, d. The temperature dependence of the X-ray absorption near-edge structure (XANES) spectra at Pr L2-edge was measured for the films, and the valence states of praseodymium (Pr) ion were determined using the analysis of the XANES spectra. As a result, the average valence of the Pr ion in the d = 50 nm film slightly increases with decreasing temperature from the common value of 3.0+ around room temperature to 3.15+ at 8 K. The valence shift of Pr is thus similar to what was observed on the PYCCO polycrystalline bulks with an abrupt metal-insulator transition, accompanied by a spin-state (SS) transition of Co ions. Furthermore, the low-temperature SQUID measurements evidenced a paramagnetic behavior down to the lowest temperature, which suggests that the dominant part of Co3+ ions in the film grown on the SLAO substrate tends to be in the low spin state characteristic for the insulating ground state. These results strongly suggest that the anomalous ρ(T) upturn in the thin films on the SrLaAlO4 (SLAO) substrate is closely related to the SS transition of Co ions. On the other hand, PYCCO films grown on the LaAlO3 (LAO) substrate that applied an in-plane tensile stress showed no valence shift of Pr ions and developed a long range ferromagnetic order, which points to a complete suppression of the low-temperature transition. The behaviors of the epitaxial films are discussed in terms of the in-plane stress exerted by different substrates and accumulated elastic energy.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.