Electrical properties of triple-doped bismuth oxide electrolyte for solid oxide fuel cells

Abstract

ABSTRACTIn this study, the quaternary solid solutions of (Bi2O3)(0.8−x)(Tb4O7)0.1(Ho2O3)0.1(Dy2O3)x (x = 0.05, 0.10, 0.15, 0.20) as an electrolyte were synthesized for solid oxide fuel cells by the technique of solid-state synthesis.The products were characterized by X-ray powder diffraction, differential thermal analysis/thermal gravimetry and the four-point probe technique (4PPT). The total electrical conductivity is measured on the temperature and the doped concentration by 4PPT.All samples have been obtained as the δ-phase. According to the measurements of the 4PPT, the electrical conductivities of the samples increase with the temperature but decrease with the amount of doping rate. The value of the highest conductivity (σ) is found as 1.02 × 10−1 S cm−1 for the system of (Bi2O3)0.75(Tb4O7)0.1(Ho2O3)0.1(Dy2O3)0.05 at 850 °C. The thermal gravimetry (TG) curve shows that there is no mass loss of sample during the measurement. The analyses of differential thermal reveal that there are neither endothermic peaks nor exothermic peaks during the heating and cooling cycles (ranging from 30 to 1000 °C).