Abstract
BaBi4Ti4–5/4xNbxO15 (BBNTx, x=0, 0.05, 0.15, 0.30) ceramics have been prepared by solid state method. XRD data indicate the formation of single-phase-layered perovskites for all compositions. SEM micrographs suggest that the grain size decreases with Nb doping. The effect of niobium doping on the dielectric and relaxor behavior of BaBi4Ti4O15 ceramics was investigated in a wide range of temperatures (20–777°C) and frequencies (1.21kHz to 1MHz). Nb doping influences Tc decrease as well as the decrease of dielectric permittivity at Curie temperature. At room temperature, undoped BaBi4Ti4O15 exhibits dielectric constant of ∼204 at 100kHz, that slightly increases with Nb doping. The conductivity of BBNT5 ceramics is found to be lower than that of other investigated compositions. The value of activation energy of σDC was found to be 0.89eV, 1.01eV, 0.93eV and 0.71eV for BBT, BBNT5, BBNT15 and BBNT30, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.