Abstract
High temperature superconductor NdBa2Cu3O7−δ/poly(vinyl chloride) (Nd123/PVC) composites have been prepared by cold press and hot press methods. Addition of PVC resulted in increase of the electrical resistivity with percolation occurring between 0.3 and 0.5 Nd123 volume fraction for both preparation methods. Although the samples showed some form of magnetic levitation at liquid nitrogen temperature, they do not show any zero-resistance temperature indicating the lack of effective superconducting percolative path. The density deviates from the linear calculated value with increasing Nd123 content at 0.3 volume fraction for the cold press and at 0.6 for the hot pressed samples due to increasing porosity. X-ray powder diffraction patterns suggest that the Nd123 crystals tend to align when the composites are prepared by hot press method. A resistance anomaly is observed at 90 K in the hot press composites indicating improved electrical contact between the aligned Nd123 grains. The longitudinal modulus increases as Nd123 content is increased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.