In this work, hydrothermal synthesis and ceramic sintering process were applied to fabricate (1−x)Pb(Zr0.52Ti0.48)O3−(x)CoFe2O4 (PZT–CFO) (x=0.20, 0.35, and 0.50) magnetoelectric (ME) composites. The X-ray diffraction (XRD) studies revealed that no chemical reaction occurred between individual PZT and CFO phases and confirmed the manifestation of PZT and CFO phases within the ME composite. Scanning electron microscopy (SEM) was used to investigate the microstructure and connectivity scheme in the ME composites. The dielectric constant (ε) and loss tangent (tan δ) were determined as functions of frequency and temperature for all the composites prepared. The polarization–electric field (P–E) and magnetization–magnetic field (M–H) hysteresis loops obtained indicate that both ferroelectric and ferromagnetic properties coexist in the ME composites prepared. The direct (DME) and converse magnetoelectric effects (CME) were measured only for the PZT–CFO20 (20 mol% CoFe2O4) composite sintered at 1100 °C for 4 h. The maximum values of ME voltage coefficient αME(dE/dH) and ME susceptibility coefficient αme (dH/dE) were 226 mV cm−1 Oe−1 at frequency of 75.1 kHz and 1.15×10−8 s/m at frequency of 66.8 kHz, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.