Abstract
Polycrystalline sample of (Na0·5Bi0·5)TiO3 was prepared using a high temperature solid-state reaction synthesis at 1070°C and subsequent sintering at 1100°C in oxygen atmosphere. X-ray diffraction (XRD) analysis of (Na0·5Bi0·5)TiO3 powder indicated the formation of a single phase rhombohedral structure. Dielectric study revealed the diffuse phase transition at 340°C. The ac conductivity data were found to obey power law and showed negative temperature coefficient of resistance character. Complex electric modulus analysis indicated non-Debye type dielectric relaxation in the system. The ac conductivity data were used to evaluate the density of states at Fermi level, minimum hopping length and activation energy of the compound. The correlated barrier hopping model was found to successfully explain the mechanism of charge transport in (Na0·5Bi0·5)TiO3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.