Abstract
Oxygen-deficient tin oxide thin films were prepared by radiofrequency magnetron sputtering with a sintered non-stoichiometric tin oxide ceramic target under an atmosphere of various ratios of O2/Ar from pure Ar to 1:1. X-ray diffraction analysis showed that the thin films were polycrystalline with relatively strong (1 1 0), (1 0 1) and (2 1 1) diffraction peaks. Scanning electron microscopy observation revealed that the thin films prepared at different O2/Ar ratios were all of relatively dense and homogeneous structure. With increasing O2/Ar ratio, the grain size of the films decreased slightly, and their chemical composition became close to the stoichiometric SnO2; but the deposition rate as well as film thickness increased first and then decreased sharply. It was revealed that the main defect in obtained films was oxygen vacancy (VO), and as the O2/Ar ratio increased, the concentration of VO fell down monotonously, which would lead to an increased electrical resistivity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.