Abstract
The diodes-based undoped and boron (B) doped ZnO films deposited onto p-Si by sol-gel method using spin coating technique were fabricated. The morphological properties of ZnO films were analyzed by field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM) measurements. The results indicated that the surface morphology of the films was affected by the boron incorporation. The diode parameters were determined from the analysis of the measured dark current-voltage curves. The ideality factor of the diodes is higher than unity and was found to be 2.53, 2.36 and 2.17 for the undoped, 0.1% B-doped and 0.3% B-doped ZnO diodes, respectively. The obtained diode parameters like barrier height and ideality factor suggest that B dopant improves rectifying properties of the ZnO diode. The interface states density (Dit) of the diode was determined by conductance-voltage method and Dit values for the undoped, 0.1% B-doped and 0.3% B-doped ZnO diodes were found to be 8.26 × 1011 eV−1 cm−2, 9.75 × 1011 eV−1 cm−2 and 6.61 × 1011 eV−1 cm−2, respectively. The obtained results indicate that the rectifying properties of the diodes-based nanostructure B-doped ZnO can be controlled by boron dopant.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.