Abstract
AbstractSeveral polymer composites formed from nylon 6/CaCO3 with different ratios and particle sizes were prepared using modified and unmodified CaCO3 as inorganic filler. The modification of CaCO3 surfaces was carried out by adsorption of oleic acid from toluene. TGA and DSC measurements show that the glass transition temperatures reduced by the presence of inorganic filler, whereas the melting temperature did not influenced. In all prepared polymer composites, the presence of filler accelerates the degradation process of the polymer. Dielectric properties of the investigated samples were studied in the frequency range from 45 Hz to 1 MHz and at temperatures ranging between 50 and 200°C. The presence of CaCO3 led to a remarkable decrease in the conductivity of nylon 6. © 2010 Wiley Periodicals, Inc. Adv Polym Techn 28:257–266, 2009; Published online in Wiley InterScience (www.interscience.wiley.com). DOI 10.1002/adv.20165
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.