Abstract
In this work, the properties of ZnO films of 100 nm thickness, grown using atomic layer deposition (ALD) on a-(100) and c-(001) oriented Al2O3 substrate are reported. The films were grown in the same growth conditions and parameters at six different growth temperatures (Tg) ranging from 100 °C to 300 °C. All as-grown and annealed films were found to be polycrystalline, highly (001) oriented for the c-Al2O3 and highly (101) oriented for the a-Al2O3 substrate. The manifestation of semi-polar-(101) and polar (001)-oriented ZnO films on the same substrate provided the opportunity for a comparative study in terms of the influence of polarization on the electrical and structural properties of ZnO films. It was found that the concentration of hydrogen, carbon, and nitrogen impurities in polar (001)-oriented films was considerably higher than in semi-polar (101)-oriented ZnO films. The study showed that when transparent conductive oxide applications were considered, the ZnO layers could be deposited at a temperature of about 160 °C, because, at this growth temperature, the high electrical conductivity was accompanied by surface smoothness in the nanometer scale. On the contrary, semi-polar (101)-oriented films might offer a perspective for obtaining p-type ZnO films, because the concentration of carbon and hydrogen impurities is considerably lower than in polar films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.