Electrical and photovoltaic characteristics of CuInSe2 thin films processed by nontoxic Cu–In precursor solutions

Abstract

Nontoxic Cu–In solution-processed CuInSe2 absorber thin films and resultant photovoltaic cells have been investigated. Acetate-based Cu–In precursors having different Cu/In ratios of 0.8–1.2 were deposited by spin-coating and then selenized in Se atmosphere up to 550 °C. Single tetragonal CuInSe2 phase was dominantly obtained regardless of Cu/In ratios, with the segregation of Cu2−xSe secondary phase only in the case of Cu-rich films as evidenced by Raman spectra. The films with the 1.1 ratio demonstrated a larger grain size of ∼1.06 µm with an increased carrier concentration of ∼1.7 × 1018 cm−3 and a decreased band gap of ∼1.02 eV, compared to the values obtained for Cu-deficient absorber films. The resultant best cell efficiency was ∼3.1% for the absorber having the 1.1 ratio, suggesting a potential of this simple spin-coating method as an alternative to typical vacuum processes.