Abstract
We have investigated the electrical and microstructural properties of Cu-germanides formed on p-type Ge substrate as a function of rapid thermal annealing (RTA) temperature. As increasing RTA temperatures, Cu films reacted with Ge and formed Cu-germanides. The Cu3Ge phase appears to be the dominant phase along with Cu5Ge2 phase at annealing temperatures of 500 and 600 °C. The sheet resistance and specific contact resistivity were investigated as a function of germanide formation temperature. A minimum specific contact resistivity value of 6.19´10-6 Wcm2 is obtained after annealing at 400 °C associated with the formation of low stoichiometric Cu3Ge phase. The sheet resistance and specific contact resistivity increased after rapid thermal annealing at temperatures >500 °C, indicated the degradation of the contact properties and could be associated with the formation of copper rich Cu5Ge2 phase and the loss of structural integrity with increasing annealing temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.