Elastic-Plastic Fracture Mechanics Analysis of Cast Stainless Steel Pipes (Influence of Axial Load on Z-Factor of Pipes With Circumferential Crack Under Bending Load)

Abstract

Since the ductility of cast austenitic stainless steel pipes decreases due to thermal aging embrittlement after long term operation, not only plastic collapse failure but also unstable ductile crack propagation (elastic-plastic failure) should be taken into account for the structural integrity assessment of cracked pipes. In the ASME Section XI, the load multiplier (Z-factor) is used to derive the elastic-plastic failure of the cracked components. The Z-factor of cracked pipes under bending load has been obtained without considering the axial load. In this study, the influence of the axial load on Z-factor was quantified through elastic-plastic failure analyses under various conditions. It was concluded that the axial load increased the Z-factor; however, the magnitude of the increase was not significant, particularly for the main coolant pipes of PWR nuclear power plants.