Abstract
Silica borotellurite glasses doped with different molar fraction of V2O5 have been prepared by melt quenching technique. The elastic properties of {[(TeO2)0.7 (B2O3)0.3]0.8(SiO2)0.2}(1-x)(V2O5)x glasses are investigated using ultrasonic pulse echo measurements and their elastic properties have been characterized at room temperature. The density of the glasses was measured by Archimedes method using distilled water as buoyant liquid. The ultrasonic wave velocities (longitudinal, vl and shear, vS) were recorded at 5 MHz. Elastic moduli, Poisson’s ratio (σ) and microhardness (H) were then calculated to obtain quantitative analysis regarding the structure of these glasses. The results obtained showed that the doping of V2O5 with silica borotellurite enhances the strengthening of glass network. Glass with 0.03 molar fraction of V205 shows low ultrasonic velocities and low elastic moduli. The variation of elastic properties is related to the change of structure in the vanadium doped silica-borotellurite glass system.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.