Abstract
AbstractSilver-nickel multilayers were prepared by sputtering at 100 K. X-ray diffraction, electrical resistivity and dimensional variation measurements were performed to structurally characterize these stratified materials, both in the as-prepared state and during the course of annealing cycles. Clearly, polycrystalline superlattices with marked (111) texture perpendicular to the strata are formed. We studied the elastic properties of these superlattices by performing uniaxial tension tests. No deviation from linear elasticity was observed, whatever the period. Young's modulus was found to be 130±15 GPa for all the periods studied. Thus no significant functional dependence of Young's modulus on the stacking periodicity exists in the AgNi superlattice, in the range of periods explored, 2.6 to 18 nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.