Abstract
AbstractFour different SiOC glass ceramics were synthesized and their fracture toughness (KIc) and fracture surface energy (γ) were assessed by means of the single‐edge precracked beam (SEPB) method. In addition, the elastic moduli were measured and the Vickers indentation behavior (hardness and microcracking) was characterized. In particular, the dependence of KIc on the free carbon content and on the fraction of crystallized nanoparticles (SiC, ZrO2, HfO2) was investigated. An increase in KIc, from about 0.73 to 0.99 MPa √m is observed as the free carbon content is increased from less than 1 to 12 vol%. The addition of Hf and Zr (resulting in 4.5 to 7.8 vol% HfO2 and ZrO2 nanoparticles) was found to increase KIc to an extent similar to the free carbon content. Moreover, predicted KIc values, assuming that the crack travels through all phases accounting for their respective volume fractions, disrupting the weakest links within the structural units, are in agreement with the experimental values.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.