Abstract
ABSTRACTIn order to develop a novel proton conductive membrane for proton exchange membrane fuel cell (PEMFC), a poly(vinyl di-fluoride) (PVDF) matrix was irradiated with swift heavy ions (SHI) to obtain radically active cylindrical latent tracks in the polymer film. Styrene was then radiografted and further sulfonated into these irradiated cylindrical regions, leading to sulfonated polystyrene (PVDF-g-PSSA) domains within PVDF. The role of the grafting degree and fluence of irradiation of the PVDF matrix on PVDF-g-PSSA membranes properties (chemical composition, ion exchange capacity) was investigated. Then, a membrane-electrode assembly (MEA) was prepared and fuel cell tests have been performed. Our results clearly show that PVDF-g-PSSA membranes with a grafting degree of about 140%, obtained after irradiation at a fluence of 1010 ions/cm2, exhibit good conductivity values but their durability is limited to about 70 h. Decreasing the fluence leads to membranes with lower grafting yield but with fuel cell performances closer to those of 140% grafted PVDF-g-PSSA membrane and improved mechanical properties. Then, ion track grafting technique is a promising technique to obtain PEM with a good trade-off between proton conductivity and mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.