Abstract
Efficient inorganic perovskite light-emitting diodes (PeLEDs) with an ultrathin perovskite emission layer (∼30 nm) were realized by doping Lewis base polyethylene glycol (PEG) into CsPbBr3 films. PEG in the perovskite films not only physically fills the crystal boundaries but also interacts with the perovskite crystals to passivate the crystal grains, reduce nonradiative recombination, and ensure efficient luminance and high efficiency. As a result, promoted brightness, current efficiency (CE), and external quantum efficiency (EQE) were achieved. The nonradiative decay rate of the PEG:CsPbBr3 composite film is 1 order of magnitude less than that of the neat CsPbBr3 film. After further optimization of the molar ratio between CsBr and PbBr2, a peak CE of 19 cd/A, a maximum EQE of 5.34%, and a maximum brightness of 36600 cd/m2 were achieved, demonstrating the interaction between PEG and the precursors. The results are expected to offer some helpful implications in optimizing the polymer-assisted PeLEDs with ultrathin emission layers, which might have potential application in see-through displays.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.