Efficient indium tin oxide/Cr-doped-TiO 2 multilayer thin films for H 2 production by photocatalytic water-splitting

Abstract

Cr-doped-TiO 2 thin films, with three different Cr concentrations (2, 5.5, and 9 at.%), have been synthesized by radio-frequency magnetron sputtering in order to sensitize TiO 2 in visible light. UV–visible spectra showed that maximum narrowing (2.1 eV) of the TiO 2 band gap is obtained for the highest Cr concentration. However, negligible photocurrent was measured with Indium Tin Oxide (ITO)/Cr-doped-TiO 2 (9 at.%) single bilayer sample due to the increased recombination rate of the photo-generated charges on the defects associated to the Cr 3+ ions. To lower the charge recombination rate in the Cr-doped-TiO 2, multilayer films with different numbers of ITO/Cr-doped-TiO 2 (9 at.%) bilayers (namely, 3-, 4-, 5-, 6- and 7-bilayers) were deposited by keeping the total thickness of TiO 2 constant in each multilayer film. When the multilayer films were exposed to visible light, we observed that the photocurrent increases as function of the number of bilayers by reaching the maximum with 6-bilayers of ITO/Cr-doped-TiO 2. The enhanced photocurrent is attributed to: 1) higher absorption of visible light by Cr-doped-TiO 2, 2) number of space charge layers in form of ITO/TiO 2 interfaces in multilayer films, and 3) generation of photoelectrons just in/or near to the space charge layer by decreasing the Cr-doped-TiO 2 layer thickness. The reduced charge recombination rate in multilayer films was also confirmed by studying the photocurrent kinetic curve. The superior photocatalytic efficiency of the 6-bilayers film implies higher hydrogen production rate through water-splitting: we obtained indeed 24.4 μmol/h of H 2 production rate, a value about two times higher than that of pure TiO 2 (12.5 μmol/h).