Abstract
High-performance undoped white organic light-emitting diode (OLED) has been fabricated using an ultrathin yellow-emitting layer of 5,6,11,12-tetraphenylnaphthacene (rubrene) inserted at two sides of interface between two N,N′-bis-(1-naphthyl)-N,N′- biphenyl-1,1′-biphenyl-4,4′- diamine (NPB) layers as a hole transporting and blue emissive layer, respectively. The results showed that a maximum luminance of the device reached to as high as 21,500 cd/m 2 at 15 V. The power efficiencies of 2.5 and 1.6 lm/W at a luminance of 1000 and 10000 cd/m 2, respectively, were obtained. The peaks of electroluminescent (EL) spectra locate at 429 and 560 nm corresponding to the Commissions Internationale De L’Eclairage (CIE) coordinates of (0.32, 0.33), which is independent of bias voltage. The performance enhancement of the device may result from direct charge carrier trapping in rubrene. Energy transfer mechanism was also found in the EL process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.