Abstract
The study of the parameters of energy harvesting and storage in the lead-free solid solution BaTi0.86Sn0.14O3 (BTSnO) was performed. The permittivity shows the behavior similar to a diffuse phase transition with the critical exponent γ = 1.84, which is close to the value characteristic of relaxors. Large values of the recoverable energy density, Wrec=(5.8–7.0)∙104 J/m3, and the energy storage efficiency coefficient, η=(82–94) %, are implemented in a wide temperature range, 30–87°С, at a low electric field, E = 18.5 kV/cm. For the first time, the analysis of the Olsen cycle was performed using two phase diagrams: polarization – electric field and entropy – temperature. A fairly good agreement was found between the values of the energy conversion density, ND ≈ 0.15 J/cm3, which was determined using two approaches. A universal parameter is proposed for comparing the energy harvesting density for the materials studied in different ranges of temperature and electric fields.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.