Efficiency of catalytic processes for the reduction of CO and VOC emissions from wood combustion in domestic fireplaces

Abstract

Pollutant characterization of domestic fireplaces, according to two paces of functioning (normal and low-charge phase) was performed. Two catalysts supported on cordierite or metal were placed in the exhaust of two domestic fireplaces (old and new generation) in order to reduce gaseous pollutants. Active phase of catalysts is composed of noble metals (Pd, Pt) and cerium. Methane was the dominant compound of the released Volatile Organic Compounds (VOC, 80% b. v.). Products resulting from incomplete combustion (CO and other VOC) did not represent more than 6% of the initial carbon content in wood. Lower concentration of CO in the exhaust was obtained with the new generation fireplace as compared to the older one with mean concentrations of CO normalized for 13% oxygen b.v. equal to 0.12% and 0.3%, respectively. Emission of VOC is also drastically reduced for new generation fireplace. The presence of a catalyst induced a decrease of the CO and VOC emission factors during ignition and low-charge phases by factors ranging from 65% to 70%. The abatement of VOC for the old generation fireplace was better in the presence of metal as compared to cordierite, with efficiency values of 65% and 30%, respectively. The new fireplace was the one on which the addition of the cleanup implements had most impact. Besides the introduction of a catalyst, a heating system of the fume was set up below the catalyst. This heating system allowed a faster activation of the catalyst, particularly during ignition and low-charge phases. Best abatements were obtained with the heated metallic support with values close to 80% and 94% for VOC and CO respectively.