Abstract
Microwave dielectric ceramics with high relative permittivity (εr) are commonly used for the miniaturation of microwave devices. The dielectric loss mechanism of microwave dielectric ceramics, as well as the property modification, has been a concerned topic among scholars. Herein, the lattice structure, defects, and broadband dielectric response of Zr4+ and Hf4+ substituted Ba4Sm9.33Ti18O54 (BST) ceramics are systematically examined. The negative temperature coefficient of resonant frequency (τf) of BST ceramics can be tuned to near zero via ion substitution, owing to the Sm2Ti2O7 second phase with a large positive τf. Optimal microwave dielectric properties of εr = 81.3, Q × f = 10,800 GHz, and τf = −4.6 ppm/°C are achieved. The lattice vibration behavior and defect concentration are analyzed by Raman spectra and thermally stimulated depolarization currents (TSDC), respectively. The increasing volume of the unit cell and TiO6 octahedra, which is because of the large-radius substitution ions, leads to an increase in lattice vibration damping factor and the generation of more oxygen vacancies (VO∙∙). Therefore, the dielectric losses in the microwave and terahertz (THz) bands increase after substitution. Meanwhile, the low-frequency dielectric losses at high temperatures also increase due to the weak restraint of carriers by the lattice. The broadband loss mechanism of Zr4+ and Hf4+ substituted BST ceramics related to lattice vibration and defects might be referenced for developing low-loss dielectric ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.