Abstract
Abstract The effects of the Zn content on the mechanical and corrosion properties of MgZnMnCa alloys were investigated. The results revealed that with increasing Zn content up to 4 wt.%, the Mg-4Zn-0.2Mn-0.2Ca (wt.%) alloy after solution treatment at 400°C for 24 h (ZM40-S) exhibited a volume fraction of 1.56 ± 0.05 (vol.%) of secondary phases with an average grain size of 83.6 ± 1.6 µm. This alloy in the at-cast condition exhibited indentation hardness (Hit) of 657.1 ± 17.8 MPa, which increased to 723.5 ± 29.8 MPa after solution treatments. In addition, the alloy also exhibited a Vickers hardness value of 66.8 ± 2.7 HV and an elastic modulus of 33.8 ± 0.6 GPa, close to the values for human bone. Further, the corrosion properties of this alloy were analyzed: it exhibited a cathodic polarization curve attributed to a hydrogen evolution reaction and an anodic curve corresponding to a passivation tendency, indicating the formation of an oxide layer at the surface; further, its corrosion rate was 0.23 mm/year.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.