Abstract
The effects of electroplated and hot-dip zinc coatings on the fracture of low-alloy steel AISI 4140 bars tempered to hardnesses in the range Rc 33 to 49 were studied. Either electroplated or hot-dip zinc coatings decrease resistance to stress corrosion cracking,i.e., they reduceKsc, the threshold stress intensity for stress corrosion cracking in 3.5 wt pct NaCl solution. AboveKscelectroplated-zinc coatings do not appear to affect the crack-growth rate, although the incubation period prior to the onset of crack growth is reduced. Hot-dip zinc coatings increase stress corrosion crack growth rates slightly because of the additive effect of internal dissolved hydrogen. Hot-dip zinc coatings reduce the critical stress intensity for fracture in the absence of a corrosive environment because of embrittlement by internal hydrogen which is released from traps during hot-dip coating and confined by the inter metallic coatings which form on the steel surface in the hot dip bath. A simple fracture mechanics analysis indicates that either increasing diameter or the presence of a zinc coating lowers the critical hardness at which the stress corrosion cracking of structural bolts can occur.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.