Abstract
0.03Pb(Sb0.5Nb0.5)O3-0.03Pb(Mn1/3Nb2/3)O3-(0.94-x)PbTiO3-xPbZrO3 ceramics doped with Y2O3 were synthesized by conventional bulk ceramic processing technique. Phases analysis, microstructures and piezoelectric properties were investigated as a function of Y2O3 contents (0.03, 0.05, 0.1 0.3, 0.5 and 0.7 wt.%). Microstructures and phases information were characterized using a scanning electron microscope (SEM) and an X-ray diffractometer (XRD). Relative dielectric constant (K33 T) and coupling factor (kp) were obtained from the resonance measurement method. Both K33 T and kp were shown to reach to the maximum at 0.1wt.% Y2O3. In order to evaluate the stability of resonance frequency and effective electromechanical coupling factor (Keff) as a function of Y2O3 contents under strong electric field, the variation of resonance and anti-resonance frequency were also measured using a high voltage frequency response analyzer(FRA5096) under various alternating electric fields from 10V/mm to 80V/mm. It was shown that the effective electromechanical coupling factor was stabilized along with increasing Y2O3 contents.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.